Abdi ATILGAN [1] , Hüseyin PEKER [2] , Hüseyin TAN [3] , Davut BAKIR [4]


This study was performed to determine the effects of impregnation with boron compounds and water repellents on the dimensional stability of wood. For this purpose,  the test specimens prepared from scotch pine (Pinus sylvestris L.) wood  which met the requirements of TS 345 and TS 1476 standards procedures were single, double or multi treated according to  ASTM D 1413-76 standard procedure with some boron compounds such as boric acid (Ba) and borax (Bx), some water repellent materials (WRM) such as styrene, methyl methacryrilate, izocyonate, polyethyleneglychol-400 (PEG-400), and some  commercial impregnation materials such as Tanalith-CBC (T-CBC), ammonium sulfate (AS), diamonium phosphate (DAP), and vacsol. As a result, secondary treatment with WRM decreases amount of leached material. Water absorption ratio of wood was lowest in the treatment only with WRM, boron compounds and   in secondary treatment of PEG-400 with WRM. Order of convenience for dimensional stability was like WRM>(Ba+Bx)+WRM>PEG-400+WRM>commercial impregnation materials. Order of convenience for volumetric shrinkage efficiency was like (Ba+Bx)+WRM>PEG-400+WRM>AS, DAP, T-CBC. WRM was found more successful in leaching prevention when used as a secondary treatment after PEG-400. So, the wood which will be used in open air and high relative humidity conditions, secondary impregnation with WRM is recommended.
Bu çalışmada, odun koruma ve çalışmayı azaltma amacıyla kullanılan bazı kimyasal maddelerin emprenye maddesi yıkanması ve hacimsel stabiliteye etkileri araştırılmıştır. Bu maksatla, sarıçam (Pinus sylvestris L.) odunundan TS 345 ve TS 1476’ya göre hazırlanan örnekler, ASTM D 1413-76 esaslarına göre; Borik asit (Ba), Boraks (Bx), Polietilenglikol 400 (PEG-400) ve bazı borlu bileşiklerden; Ba+Bx, Ba+Bx+St, Ba+Bx+MMA, Ba+Bx+St+MMA, su itici maddelerden (SİM); Stiren (St), Metilmetakrilat (MMA), İzosiyanat (ISO), ticari emprenye maddelerinden; Tanalith-CBC (T-CBC), Amonyum sülfat (AS), Diamonyum fosfat (DAP) ve Vacsol (V) ile tekli, ikili veya çoklu işlemler halinde emprenye edildikten sonra AWPA N-10 ve ASTM D 1413-76 esaslarına uyularak 6, 24, 48 ve 72 saat süreyle yıkanma etkisinde bırakılmıştır. Yıkanma etkisi sonucu boyutsal çalışma ve emprenye maddesi yıkanma miktarlarına göre; yıkanma süresi arttıkça yıkanan madde miktarı azalmıştır. Borlu bileşikler ve bunların ikincil SİM işlemli uygulamaları yıkanan madde miktarını azaltmıştır. Su alma oranları zamana bağlı olarak artmakta, en az su alma oranı SİM’lerin tek başına kullanımında ve Borlu bileşikler ile PEG-400’ün SİM’ler ile ikincil işlemli emprenyesinde elde edilmiştir. Odunda stabilite sağlamada uygunluk sırası; SİM>Ba+Bx+SİM>PEG– 400+SİM>Ticari emprenye maddeleri şeklinde olmuştur. Hacimsel daralmayı azaltıcı etkenlik bakımından uygunluk sırası; (Ba+Bx)+SİM>PEG–400+SİM>AS, DAP, T-CBC şeklindedir. Su itici etkenlik değeri bakımından, PEG-400’ün SİM’li uygulamaları başarılı bulunmuştur. SİM’lerin yıkanmayı engelleme etkenliğinin PEG-400’lü gruplarla emprenyede daha başarılı olduğu söylenebilir. Buna göre; açık hava yada yüksek nem şartlarında kullanılacak ve su etkisi ile odundan yıkanarak uzaklaşabilecek suda çözünen borlu bileşikler ile emprenye edilmiş sarıçam odununda emprenye maddesi yıkanmasını engellemek, su alma oranını azaltmak, su ititci etkenliği arttırmak ve boyutsal stabiliteyi düzenlemek maksadıyla SİM’lerle ikincil emprenye uygulamaları önerilebilir.
  • ASTM D 1413-76 (1976) Standard Test Method of Testing, Wood Preservatives by Laboratory, Soilblock Cultures, Annual Book of ASTM Standards, 452- 460 p.
  • Hofors B (1990) The Role of the Wosa in the Development of PEG Preservation R.M. Rowel R.J Barbour, Eds. Advance in Chemistry Series, 5: 195- 217.
  • Murphy RJ, Barnes HM, Gray S (1990). The Efficacy of Boron Polymer Systems: A preliminary Report on Laboratory Studies, Forest Products Research Society, 142.
  • Richardson BA (1987) Wood Preservation, Construction Press, Ltd. 238 p., Lancaster
  • Stamm AJ, Honsen LA (1935) Minimizing Wood Shrinkage and Swelling, G. Ind. and Eng. Cham., 6:201-204.
  • Stamm AJ (1959) Effect of Polyethilene Glycol on the Dimensional Stability of Wood, Forest Prod. Journal, 9: 375-381
  • TS 345 (1974) A Testing Methods for the Effects of Wood Impregnating Substances. Turkish Standards.
  • TS 4176 (1984) Wood-Sampling Sample Tress and Log for Determination of Physical and Mechanical Properties of Wood in Homogeneous Stands. Turkish Standards.
  • Voulgaridis E (1986) Effect of Water Temperature and Melting Point of Wax on Water Repellency in Treated Wood, Holz Forschung und Holz Verwertung, 6: 141-144
  • Williams LH (1990) Potential Benefits of Diffusible Preservatives for Wood Protection, an Analysis with Emphasis on Building Protection with Diffusible Preservatives, Forest Product Research Society, 29-35.
  • Yalınkılıç MK, Baysal E, Demirci Z (1997) Leaching from Wood after Impregnated with Boron Compounds and Increasing Dimensional Stability by Prevention of Leaching with Various Hydrophobic Materials, Turkish Journal Agriculture and Forestry, 21: 423-431. of
  • Yıldız ÜC (1992) Ağaç Malzemenin Yapısında Değişiklerle Özelliklerinin ORENKO-92, I. Ulusal Orman Ürünleri Endüstrisi Kongresi Bildiri Metinleri, 1: 403, Trabzon (In Turkish)
Primary Language en
Journal Section Research Article
Authors

Author: Abdi ATILGAN

Author: Hüseyin PEKER

Author: Hüseyin TAN

Author: Davut BAKIR

Dates

Publication Date : February 7, 2012

Bibtex @ { artvinofd29806, journal = {Artvin Çoruh Üniversitesi Orman Fakültesi Dergisi}, issn = {2146-1880}, eissn = {2146-698X}, address = {}, publisher = {Artvin Çoruh University}, year = {2012}, volume = {12}, pages = {126 - 138}, doi = {}, title = {The Possibilities of Using Boron Compounds in Environmentally Friendly Furniture Industry}, key = {cite}, author = {ATILGAN, Abdi and PEKER, Hüseyin and TAN, Hüseyin and BAKIR, Davut} }
APA ATILGAN, A , PEKER, H , TAN, H , BAKIR, D . (2012). The Possibilities of Using Boron Compounds in Environmentally Friendly Furniture Industry. Artvin Çoruh Üniversitesi Orman Fakültesi Dergisi , 12 (2) , 126-138 . Retrieved from http://ofd.artvin.edu.tr/en/issue/2263/29806
MLA ATILGAN, A , PEKER, H , TAN, H , BAKIR, D . "The Possibilities of Using Boron Compounds in Environmentally Friendly Furniture Industry". Artvin Çoruh Üniversitesi Orman Fakültesi Dergisi 12 (2012 ): 126-138 <http://ofd.artvin.edu.tr/en/issue/2263/29806>
Chicago ATILGAN, A , PEKER, H , TAN, H , BAKIR, D . "The Possibilities of Using Boron Compounds in Environmentally Friendly Furniture Industry". Artvin Çoruh Üniversitesi Orman Fakültesi Dergisi 12 (2012 ): 126-138
RIS TY - JOUR T1 - The Possibilities of Using Boron Compounds in Environmentally Friendly Furniture Industry AU - Abdi ATILGAN , Hüseyin PEKER , Hüseyin TAN , Davut BAKIR Y1 - 2012 PY - 2012 N1 - DO - T2 - Artvin Çoruh Üniversitesi Orman Fakültesi Dergisi JF - Journal JO - JOR SP - 126 EP - 138 VL - 12 IS - 2 SN - 2146-1880-2146-698X M3 - UR - Y2 - 2020 ER -
EndNote %0 Artvin Çoruh Üniversitesi Orman Fakültesi Dergisi The Possibilities of Using Boron Compounds in Environmentally Friendly Furniture Industry %A Abdi ATILGAN , Hüseyin PEKER , Hüseyin TAN , Davut BAKIR %T The Possibilities of Using Boron Compounds in Environmentally Friendly Furniture Industry %D 2012 %J Artvin Çoruh Üniversitesi Orman Fakültesi Dergisi %P 2146-1880-2146-698X %V 12 %N 2 %R %U
ISNAD ATILGAN, Abdi , PEKER, Hüseyin , TAN, Hüseyin , BAKIR, Davut . "The Possibilities of Using Boron Compounds in Environmentally Friendly Furniture Industry". Artvin Çoruh Üniversitesi Orman Fakültesi Dergisi 12 / 2 (February 2012): 126-138 .
AMA ATILGAN A , PEKER H , TAN H , BAKIR D . The Possibilities of Using Boron Compounds in Environmentally Friendly Furniture Industry. AÇÜOFD. 2012; 12(2): 126-138.
Vancouver ATILGAN A , PEKER H , TAN H , BAKIR D . The Possibilities of Using Boron Compounds in Environmentally Friendly Furniture Industry. Artvin Çoruh Üniversitesi Orman Fakültesi Dergisi. 2012; 12(2): 138-126.