The Possibilities of Using Boron Compounds in Environmentally Friendly Furniture Industry
Çevre Dostu Borlu Bileşiklerin Mobilya Endüstrisinde Kullanım Olanakları

Abdi Atılgan [1] , Hüseyin Peker [2] , Hüseyin Tan [3] , Davut Bakır [4]

264 697

This study was performed to determine the effects of impregnation with boron compounds and water repellents on the dimensional stability of wood. For this purpose,  the test specimens prepared from scotch pine (Pinus sylvestris L.) wood  which met the requirements of TS 345 and TS 1476 standards procedures were single, double or multi treated according to  ASTM D 1413-76 standard procedure with some boron compounds such as boric acid (Ba) and borax (Bx), some water repellent materials (WRM) such as styrene, methyl methacryrilate, izocyonate, polyethyleneglychol-400 (PEG-400), and some  commercial impregnation materials such as Tanalith-CBC (T-CBC), ammonium sulfate (AS), diamonium phosphate (DAP), and vacsol. As a result, secondary treatment with WRM decreases amount of leached material. Water absorption ratio of wood was lowest in the treatment only with WRM, boron compounds and   in secondary treatment of PEG-400 with WRM. Order of convenience for dimensional stability was like WRM>(Ba+Bx)+WRM>PEG-400+WRM>commercial impregnation materials. Order of convenience for volumetric shrinkage efficiency was like (Ba+Bx)+WRM>PEG-400+WRM>AS, DAP, T-CBC. WRM was found more successful in leaching prevention when used as a secondary treatment after PEG-400. So, the wood which will be used in open air and high relative humidity conditions, secondary impregnation with WRM is recommended.
Bu çalışmada, odun koruma ve çalışmayı azaltma amacıyla kullanılan bazı kimyasal maddelerin emprenye maddesi yıkanması ve hacimsel stabiliteye etkileri araştırılmıştır. Bu maksatla, sarıçam (Pinus sylvestris L.) odunundan TS 345 ve TS 1476’ya göre hazırlanan örnekler, ASTM D 1413-76 esaslarına göre; Borik asit (Ba), Boraks (Bx), Polietilenglikol 400 (PEG-400) ve bazı borlu bileşiklerden; Ba+Bx, Ba+Bx+St, Ba+Bx+MMA, Ba+Bx+St+MMA, su itici maddelerden (SİM); Stiren (St), Metilmetakrilat (MMA), İzosiyanat (ISO), ticari emprenye maddelerinden; Tanalith-CBC (T-CBC), Amonyum sülfat (AS), Diamonyum fosfat (DAP) ve Vacsol (V) ile tekli, ikili veya çoklu işlemler halinde emprenye edildikten sonra AWPA N-10 ve ASTM D 1413-76 esaslarına uyularak 6, 24, 48 ve 72 saat süreyle yıkanma etkisinde bırakılmıştır. Yıkanma etkisi sonucu boyutsal çalışma ve emprenye maddesi yıkanma miktarlarına göre; yıkanma süresi arttıkça yıkanan madde miktarı azalmıştır. Borlu bileşikler ve bunların ikincil SİM işlemli uygulamaları yıkanan madde miktarını azaltmıştır. Su alma oranları zamana bağlı olarak artmakta, en az su alma oranı SİM’lerin tek başına kullanımında ve Borlu bileşikler ile PEG-400’ün SİM’ler ile ikincil işlemli emprenyesinde elde edilmiştir. Odunda stabilite sağlamada uygunluk sırası; SİM>Ba+Bx+SİM>PEG– 400+SİM>Ticari emprenye maddeleri şeklinde olmuştur. Hacimsel daralmayı azaltıcı etkenlik bakımından uygunluk sırası; (Ba+Bx)+SİM>PEG–400+SİM>AS, DAP, T-CBC şeklindedir. Su itici etkenlik değeri bakımından, PEG-400’ün SİM’li uygulamaları başarılı bulunmuştur. SİM’lerin yıkanmayı engelleme etkenliğinin PEG-400’lü gruplarla emprenyede daha başarılı olduğu söylenebilir. Buna göre; açık hava yada yüksek nem şartlarında kullanılacak ve su etkisi ile odundan yıkanarak uzaklaşabilecek suda çözünen borlu bileşikler ile emprenye edilmiş sarıçam odununda emprenye maddesi yıkanmasını engellemek, su alma oranını azaltmak, su ititci etkenliği arttırmak ve boyutsal stabiliteyi düzenlemek maksadıyla SİM’lerle ikincil emprenye uygulamaları önerilebilir.
  • ASTM D 1413-76 (1976) Standard Test Method of Testing, Wood Preservatives by Laboratory, Soilblock Cultures, Annual Book of ASTM Standards, 452- 460 p.
  • Hofors B (1990) The Role of the Wosa in the Development of PEG Preservation R.M. Rowel R.J Barbour, Eds. Advance in Chemistry Series, 5: 195- 217.
  • Murphy RJ, Barnes HM, Gray S (1990). The Efficacy of Boron Polymer Systems: A preliminary Report on Laboratory Studies, Forest Products Research Society, 142.
  • Richardson BA (1987) Wood Preservation, Construction Press, Ltd. 238 p., Lancaster
  • Stamm AJ, Honsen LA (1935) Minimizing Wood Shrinkage and Swelling, G. Ind. and Eng. Cham., 6:201-204.
  • Stamm AJ (1959) Effect of Polyethilene Glycol on the Dimensional Stability of Wood, Forest Prod. Journal, 9: 375-381
  • TS 345 (1974) A Testing Methods for the Effects of Wood Impregnating Substances. Turkish Standards.
  • TS 4176 (1984) Wood-Sampling Sample Tress and Log for Determination of Physical and Mechanical Properties of Wood in Homogeneous Stands. Turkish Standards.
  • Voulgaridis E (1986) Effect of Water Temperature and Melting Point of Wax on Water Repellency in Treated Wood, Holz Forschung und Holz Verwertung, 6: 141-144
  • Williams LH (1990) Potential Benefits of Diffusible Preservatives for Wood Protection, an Analysis with Emphasis on Building Protection with Diffusible Preservatives, Forest Product Research Society, 29-35.
  • Yalınkılıç MK, Baysal E, Demirci Z (1997) Leaching from Wood after Impregnated with Boron Compounds and Increasing Dimensional Stability by Prevention of Leaching with Various Hydrophobic Materials, Turkish Journal Agriculture and Forestry, 21: 423-431. of
  • Yıldız ÜC (1992) Ağaç Malzemenin Yapısında Değişiklerle Özelliklerinin ORENKO-92, I. Ulusal Orman Ürünleri Endüstrisi Kongresi Bildiri Metinleri, 1: 403, Trabzon (In Turkish)
Birincil Dil en
Konular
Dergi Bölümü Araştırma Makalesi
Yazarlar

Yazar: Abdi Atılgan

Yazar: Hüseyin Peker

Yazar: Hüseyin Tan

Yazar: Davut Bakır

Bibtex @ { artvinofd29806, journal = {Artvin Çoruh Üniversitesi Orman Fakültesi Dergisi}, issn = {2146-1880}, eissn = {2146-698X}, address = {Artvin Çoruh Üniversitesi}, year = {2012}, volume = {12}, pages = {126 - 138}, doi = {}, title = {The Possibilities of Using Boron Compounds in Environmentally Friendly Furniture Industry}, key = {cite}, author = {Atılgan, Abdi and Peker, Hüseyin and Tan, Hüseyin and Bakır, Davut} }
APA Atılgan, A , Peker, H , Tan, H , Bakır, D . (2012). The Possibilities of Using Boron Compounds in Environmentally Friendly Furniture Industry. Artvin Çoruh Üniversitesi Orman Fakültesi Dergisi, 12 (2), 126-138. Retrieved from http://ofd.artvin.edu.tr/issue/2263/29806
MLA Atılgan, A , Peker, H , Tan, H , Bakır, D . "The Possibilities of Using Boron Compounds in Environmentally Friendly Furniture Industry". Artvin Çoruh Üniversitesi Orman Fakültesi Dergisi 12 (2012): 126-138 <http://ofd.artvin.edu.tr/issue/2263/29806>
Chicago Atılgan, A , Peker, H , Tan, H , Bakır, D . "The Possibilities of Using Boron Compounds in Environmentally Friendly Furniture Industry". Artvin Çoruh Üniversitesi Orman Fakültesi Dergisi 12 (2012): 126-138
RIS TY - JOUR T1 - The Possibilities of Using Boron Compounds in Environmentally Friendly Furniture Industry AU - Abdi Atılgan , Hüseyin Peker , Hüseyin Tan , Davut Bakır Y1 - 2012 PY - 2012 N1 - DO - T2 - Artvin Çoruh Üniversitesi Orman Fakültesi Dergisi JF - Journal JO - JOR SP - 126 EP - 138 VL - 12 IS - 2 SN - 2146-1880-2146-698X M3 - UR - Y2 - 2019 ER -
EndNote %0 Artvin Çoruh Üniversitesi Orman Fakültesi Dergisi The Possibilities of Using Boron Compounds in Environmentally Friendly Furniture Industry %A Abdi Atılgan , Hüseyin Peker , Hüseyin Tan , Davut Bakır %T The Possibilities of Using Boron Compounds in Environmentally Friendly Furniture Industry %D 2012 %J Artvin Çoruh Üniversitesi Orman Fakültesi Dergisi %P 2146-1880-2146-698X %V 12 %N 2 %R %U
ISNAD Atılgan, Abdi , Peker, Hüseyin , Tan, Hüseyin , Bakır, Davut . "Çevre Dostu Borlu Bileşiklerin Mobilya Endüstrisinde Kullanım Olanakları". Artvin Çoruh Üniversitesi Orman Fakültesi Dergisi 12 / 2 (Şubat 2012): 126-138.